A study of white etching crack formation by compression-torsion experiments
In this study, an attempt was made to recreate the bearing damage phenomenon “White Etching Cracks” with a simplified testing setup. Rolling contact fatigue conditions were simulated with in-phase and out-ofphase cyclic compression-torsion experiments on 100Cr6 steel specimens. The results are compa...
| Main Authors: | , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Gruppo Italiano Frattura
2016-10-01
|
| Series: | Frattura ed Integrità Strutturale |
| Subjects: | |
| Online Access: | http://www.gruppofrattura.it/pdf/rivista/numero38/numero_38_art_2.pdf |
| Summary: | In this study, an attempt was made to recreate the bearing damage phenomenon “White Etching Cracks” with a simplified testing setup. Rolling contact fatigue conditions were simulated with in-phase and out-ofphase cyclic compression-torsion experiments on 100Cr6 steel specimens. The results are compared in terms of microstructural change. Focused Ion Beam and metallographic analysis reveal that a fine-grained, white etching zone formed in the vicinity of the fatigue cracks of specimens tested with the in-phase load pattern. In contrast, no such structures were found after testing the out-of-phase load pattern. The properties of the white etching zone are characterised in more detail and compared with White Etching Cracks |
|---|---|
| ISSN: | 1971-8993 1971-8993 |