The influence of TIG-Arc physical characteristics on the penetration and weld width under different Ar and He supply conditions

• Main Authors: Hongbin Dai, Xiuqiang Shen, Haoran Wang
• Format: Article
• Language: English
• Published: Elsevier 2018-06-01
• Series: Results in Physics
• Online Access: http://www.sciencedirect.com/science/article/pii/S2211379718308118

In the paper, the 5A03 aluminium alloy was employed to study the influence of TIG arc on the penetration and the weld width. And the split anode method with water-cooled copper plate was used to measure and record the distribution of arc current, under different flow ratio of argon and helium conditions. And a gas supply device controlled by a solenoid valve was employed to obtain the stable TIG welding arc of gas supply alternately at the frequency of 1 Hz and 4 Hz, and then collected the phenomenon of arc alternate by the high-speed camera. The experimental results indicated that the current density at the arc anode center of argon and helium supply alternately with different mixing ratio is lower than that of the pure argon-arc center. Nonetheless, the former is more uniform in current density within 2 mm from the arc center. Furthermore, it presented as a component arc of argon-arc and helium-arc switched, with the condition of argon and helium supply alternately at a frequency of 1 Hz and the arc power density is greater and concentrated, leading to the wider and deeper weld. Keywords: Current density, Arc shape, The penetration and weld width