Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution Treatment

Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution Treatment

Zn-Al layered double hydroxides (LDHs) were synthesized herein via a simple process. First, Al-doped ZnO film was deposited onto a glass substrate using the facing target sputtering system. Successful synthesis of the Zn–Al LDH was achieved via a treatment process using an aqueous solution which con...

Full description

Bibliographic Details
Main Authors: Jaehwan Shin, Kyunghwan Kim, Jeongsoo Hong
Format: Article
Language:English
Published: MDPI AG 2020-07-01
Series:Coatings
Subjects:
Zn–Al
layer double hydroxide
sputter
solution process
Online Access:https://www.mdpi.com/2079-6412/10/7/669
id doaj-d9b09b65c7c34ce59d0914967c626985
record_format Article
spelling doaj-d9b09b65c7c34ce59d0914967c6269852020-11-25T02:59:53ZengMDPI AGCoatings2079-64122020-07-011066966910.3390/coatings10070669Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution TreatmentJaehwan Shin0Kyunghwan Kim1Jeongsoo Hong2Department of Electrical Engineering, Gachon University, Incheon 13120, KoreaDepartment of Electrical Engineering, Gachon University, Incheon 13120, KoreaDepartment of Electrical Engineering, Gachon University, Incheon 13120, KoreaZn-Al layered double hydroxides (LDHs) were synthesized herein via a simple process. First, Al-doped ZnO film was deposited onto a glass substrate using the facing target sputtering system. Successful synthesis of the Zn–Al LDH was achieved via a treatment process using an aqueous solution which contains NO<sub>3</sub><sup>−</sup> anions. X-ray diffraction analysis confirmed that it was consistent with the previous Zn–Al LDH synthesis experiment data, and the calculated <i>d</i>-value was 9.1 Å. Scanning electron microscopy observations revealed that the as-synthesized sample had a plate-like structure.https://www.mdpi.com/2079-6412/10/7/669Zn–Allayer double hydroxidesputtersolution process
collection DOAJ
language English
format Article
sources DOAJ
author Jaehwan Shin
Kyunghwan Kim
Jeongsoo Hong
spellingShingle Jaehwan Shin
Kyunghwan Kim
Jeongsoo Hong
Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution Treatment
Coatings
Zn–Al
layer double hydroxide
sputter
solution process
author_facet Jaehwan Shin
Kyunghwan Kim
Jeongsoo Hong
author_sort Jaehwan Shin
title Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution Treatment
title_short Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution Treatment
title_full Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution Treatment
title_fullStr Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution Treatment
title_full_unstemmed Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution Treatment
title_sort zn-al layered double hydroxide thin film fabricated by the sputtering method and aqueous solution treatment
publisher MDPI AG
series Coatings
issn 2079-6412
publishDate 2020-07-01
description Zn-Al layered double hydroxides (LDHs) were synthesized herein via a simple process. First, Al-doped ZnO film was deposited onto a glass substrate using the facing target sputtering system. Successful synthesis of the Zn–Al LDH was achieved via a treatment process using an aqueous solution which contains NO<sub>3</sub><sup>−</sup> anions. X-ray diffraction analysis confirmed that it was consistent with the previous Zn–Al LDH synthesis experiment data, and the calculated <i>d</i>-value was 9.1 Å. Scanning electron microscopy observations revealed that the as-synthesized sample had a plate-like structure.
topic Zn–Al
layer double hydroxide
sputter
solution process
url https://www.mdpi.com/2079-6412/10/7/669
work_keys_str_mv AT jaehwanshin znallayereddoublehydroxidethinfilmfabricatedbythesputteringmethodandaqueoussolutiontreatment
AT kyunghwankim znallayereddoublehydroxidethinfilmfabricatedbythesputteringmethodandaqueoussolutiontreatment
AT jeongsoohong znallayereddoublehydroxidethinfilmfabricatedbythesputteringmethodandaqueoussolutiontreatment
_version_ 1724700475624783872

Similar Items