Zn-Al Layered Double Hydroxide Thin Film Fabricated by the Sputtering Method and Aqueous Solution Treatment
Zn-Al layered double hydroxides (LDHs) were synthesized herein via a simple process. First, Al-doped ZnO film was deposited onto a glass substrate using the facing target sputtering system. Successful synthesis of the Zn–Al LDH was achieved via a treatment process using an aqueous solution which con...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
MDPI AG
2020-07-01
|
| Series: | Coatings |
| Subjects: | |
| Online Access: | https://www.mdpi.com/2079-6412/10/7/669 |
| Summary: | Zn-Al layered double hydroxides (LDHs) were synthesized herein via a simple process. First, Al-doped ZnO film was deposited onto a glass substrate using the facing target sputtering system. Successful synthesis of the Zn–Al LDH was achieved via a treatment process using an aqueous solution which contains NO<sub>3</sub><sup>−</sup> anions. X-ray diffraction analysis confirmed that it was consistent with the previous Zn–Al LDH synthesis experiment data, and the calculated <i>d</i>-value was 9.1 Å. Scanning electron microscopy observations revealed that the as-synthesized sample had a plate-like structure. |
|---|---|
| ISSN: | 2079-6412 |