Improvement of die life in high speed injection die casting
High-speed injection die casting is an effi cient manufacturing technology for upgrading aluminum die-cast products. However, defi ciencies (such as die damage in early period) due to larger load on the molding die compared with conventional technology have brought new challenges. In this study, the...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Foundry Journal Agency
2008-11-01
|
| Series: | China Foundry |
| Subjects: | |
| Online Access: | http://www.foundryworld.com/uploadfile/200922748303813.pdf |
| id |
doaj-d87d265993eb40b0a354a759e2914f07 |
|---|---|
| record_format |
Article |
| spelling |
doaj-d87d265993eb40b0a354a759e2914f072020-11-24T23:48:41ZengFoundry Journal AgencyChina Foundry1672-64212008-11-0154280285Improvement of die life in high speed injection die casting Akihito HasunoJunji YoshidaYasuhiro ArisudaHigh-speed injection die casting is an effi cient manufacturing technology for upgrading aluminum die-cast products. However, defi ciencies (such as die damage in early period) due to larger load on the molding die compared with conventional technology have brought new challenges. In this study, the cause of damage generated in super high-speed injection was investigated by the combination of experimental observation of the dies and CAE simulation (e.g. die emperature analysis, fl ow analysis and thermal stress analysis). The potential countermeasures to solve the above problems were also proposed.http://www.foundryworld.com/uploadfile/200922748303813.pdfCAE simulationdie castingheat checkthermal stress |
| collection |
DOAJ |
| language |
English |
| format |
Article |
| sources |
DOAJ |
| author |
Akihito Hasuno Junji Yoshida Yasuhiro Arisuda |
| spellingShingle |
Akihito Hasuno Junji Yoshida Yasuhiro Arisuda Improvement of die life in high speed injection die casting China Foundry CAE simulation die casting heat check thermal stress |
| author_facet |
Akihito Hasuno Junji Yoshida Yasuhiro Arisuda |
| author_sort |
Akihito Hasuno |
| title |
Improvement of die life in high speed injection die casting |
| title_short |
Improvement of die life in high speed injection die casting |
| title_full |
Improvement of die life in high speed injection die casting |
| title_fullStr |
Improvement of die life in high speed injection die casting |
| title_full_unstemmed |
Improvement of die life in high speed injection die casting |
| title_sort |
improvement of die life in high speed injection die casting |
| publisher |
Foundry Journal Agency |
| series |
China Foundry |
| issn |
1672-6421 |
| publishDate |
2008-11-01 |
| description |
High-speed injection die casting is an effi cient manufacturing technology for upgrading aluminum die-cast products. However, defi ciencies (such as die damage in early period) due to larger load on the molding die compared with conventional technology have brought new challenges. In this study, the cause of damage generated in super high-speed injection was investigated by the combination of experimental observation of the dies and CAE simulation (e.g. die emperature analysis, fl ow analysis and thermal stress analysis). The potential countermeasures to solve the above problems were also proposed. |
| topic |
CAE simulation die casting heat check thermal stress |
| url |
http://www.foundryworld.com/uploadfile/200922748303813.pdf |
| work_keys_str_mv |
AT akihitohasuno improvementofdielifeinhighspeedinjectiondiecasting AT junjiyoshida improvementofdielifeinhighspeedinjectiondiecasting AT yasuhiroarisuda improvementofdielifeinhighspeedinjectiondiecasting |
| _version_ |
1725485124184702976 |