The Effect of Graphene on the Protective Properties of Water-Based Epoxy Coatings on Al2024-T3
0.5 and 1% wt. of graphene nanoflakes were added to an anticorrosive additives-free water-based epoxy resin applied to Al2024-T3 samples. Calorimetric (DSC) and adhesion (cross-cut test) tests indicated that the presence of graphene did not affect the polymerization process of the resin or its adhes...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Limited
2017-01-01
|
| Series: | International Journal of Corrosion |
| Online Access: | http://dx.doi.org/10.1155/2017/1541267 |
| Summary: | 0.5 and 1% wt. of graphene nanoflakes were added to an anticorrosive additives-free water-based epoxy resin applied to Al2024-T3 samples. Calorimetric (DSC) and adhesion (cross-cut test) tests indicated that the presence of graphene did not affect the polymerization process of the resin or its adhesion to the substrate while it had some effect on its wettability. Electrochemical Impedance Spectroscopy (EIS) results obtained suggested that the addition of a small amount of graphene greatly enhanced the protective properties of the epoxy coating, retarding electrolytes absorption and reducing the total amount of adsorbed water. The latter occurrence suggests that the graphene effect on coating performances is related to both extended diffusion pathway length and graphene/matrix interaction due to the unique properties of graphene. |
|---|---|
| ISSN: | 1687-9325 1687-9333 |