Effect of Zn and Ca Addition on Microstructure and Strength at Room Temperature of As-Cast and As-Extruded Mg-Sn Alloys

• Main Authors: Yang Zhang, Leipeng Song, Xiaoyang Chen, Yalin Lu, Xiaoping Li
• Format: Article
• Language: English
• Published: MDPI AG 2018-08-01
• Series: Materials
• Subjects: Mg-Sn alloy; as-cast; hot extrusion; microstructure; strength at room temperature
• Online Access: http://www.mdpi.com/1996-1944/11/9/1490

In this study, the effect of Zn and Ca addition on microstructure and strength at room temperature of Mg-Sn alloys was investigated by comparison of Mg-6Sn, Mg-6Sn-2Zn, and Mg-6Sn-2Zn-1Ca alloys in as-cast and as-extruded states. In the as-cast samples, α-Mg and Mg2Sn phases were the main phases of Mg-6Sn and Mg-6Sn-2Zn alloys, while the CaMgSn phase was formed in Mg-6Sn-2Zn-1Ca alloy due to the addition of the Ca element. Mg2Sn phase dissolved into the matrix during homogenization while CaMgSn phase remained. Incomplete dynamic recrystallization (DRX) took place in these alloys during hot extrusion. Fine Mg2Sn precipitates were observed in α-Mg matrix of as-extruded samples. Zn showed little influence on microstructure, whereas Ca reduced the volume fraction of un-DRXed grains and increased the size of DRXed grains. As-extruded Mg-Sn alloys exhibited typical fiber texture. The strength at room temperature of Mg-Sn alloys improved significantly after hot extrusion. The addition of Zn element was beneficial to the strength at room temperature of the Mg-6Sn alloy, while the further addition of Ca element was harmful to the strength. Among these alloys, the Mg-6Sn-2Zn alloy exhibited the best strength at room temperature in both as-cast and as-extruded states.