Toughness, Tenacity and Maximum Initial Strength of Rubber Modified Asphalt Binders
The toughness and tenacity test method, which was developed in the 1980s, is popular for evaluating a polymer-modified binder. Several states like Nevada require performing this test to evaluate non-modified binder samples, as well as other types of modified binders. In this regard, a toughness and...
| Main Authors: | , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
D. G. Pylarinos
2019-02-01
|
| Series: | Engineering, Technology & Applied Science Research |
| Subjects: | |
| Online Access: | https://etasr.com/index.php/ETASR/article/view/2526 |
| Summary: | The toughness and tenacity test method, which was developed in the 1980s, is popular for evaluating a polymer-modified binder. Several states like Nevada require performing this test to evaluate non-modified binder samples, as well as other types of modified binders. In this regard, a toughness and tenacity test was performed on rubber-modified samples produced from virgin binder PG58-28, PG64-16 and AC-20. In order to take the rubber size, type and content into account, two rubber sizes, mesh #20 and #40, two rubber types, ambient and cryogenic, and three rubber contents, 10%, 15%, and 20% were produced and tested. The results then were compared with polymer-modified and terminally blended rubber-modified samples. The results show improvement in the amount of initial maximum strength, and a decline in the magnitude of elongation, toughness and tenacity for the rubber-modified binder, compared to other types of binders.
|
|---|---|
| ISSN: | 2241-4487 1792-8036 |