Theoretical And Experimental Analysis Of Aluminium Bars Rolling Process In Three-High Skew Rolling Mill

• Main Authors: Stefanik A., Morel A., Mróz S., Szota P.
• Format: Article
• Language: English
• Published: Polish Academy of Sciences 2015-06-01
• Series: Archives of Metallurgy and Materials
• Subjects: three-high skew rolling mill; aluminum alloys; round bars; FEM; numerical analysis
• Online Access: http://www.degruyter.com/view/j/amm.2015.60.issue-2/amm-2015-0211/amm-2015-0211.xml?format=INT

Technology of round bars rolling on a three-high skew rolling mills allows rolling of standard materials such as steel and aluminum, as well as new materials, especially hard deformable materials. The paper presents the results of theoretical and experimental rolling process of aluminum bars with a diameter of 20 mm. As the stock round bars with a diameter of 25 mm made of aluminum grade 1050A and aluminum alloy grade 2017A were used. The rolling process of aluminum bars has been carried out in a single pass. The numerical analysis was carried out by using computer program Forge2011®. On the basis of theoretical research it has been determined the state of deformation, stress and temperature distribution during rolling of aluminum bars. In addition, the results of theoretical research allowed to determine the schema of the metal plastic flow in the roll gap. Verification of the theoretical research was carried out during the rolling of aluminum bars on the RSP 40/14 laboratory three-high skew rolling mill. From the finished bars were taken the samples to set the shape and compared with the results of theoretical research. Finished aluminum round bars were characterized by low ovality and good surface quality.