| Summary: | The optimization of the structural and morphological characteristics of the system constituted by molibdenum and copper indium diselenide layers deposited onto glass substrates (glass/Mo/CuInSe2) is essential for its application in efficient thin film solar cells. For developing such kind of systems, soda-lime glass substrates have been used to prepare Mo thin films by evaporation at deposition rates between 4 and 13 Å/s, and subsequently CuInSe2 layers by direct electrodeposition at 12 Å/s constant rate. The structural and morphological analysis of the samples indicated that the surface roughness of the CuInSe2 layer is minimized, and its grain size is maximized, when electrodeposition process takes place onto Mo thin films evaporated at rates higher than 8 Å/s.<br><br>La optimización de las características estructurales y morfológicas del sistema formado por películas de molibdeno y seleniuro de cobre e indio depositadas sobre sustratos de vidrio (vidrio/Mo/CuInSe2) resulta esencial para su aplicación en la formación de células solares de lámina delgada eficientes. Para el desarrollo de este tipo de sistemas se han utilizado sustratos de vidrio sodocálcico, sobre los que se han preparado láminas delgadas de Mo mediante evaporación a ritmos de crecimiento de entre 4 y 13 Å/s, y a continuación películas de CuInSe2 mediante electrodepósito directo a una velocidad constante de 12 Å/s. El análisis estructural y morfológico de las muestras preparadas indica que la rugosidad superficial de la película de CuInSe2 se minimiza, y su tamaño de grano se maximiza, cuando el electrodepósito se realiza sobre láminas delgadas de Mo evaporadas a velocidades superiores a 8 Å/s.
|
|---|