| Summary: | The aim of this study was to evaluate the influence of calcium-silicate-based sealer (Endosequence-BC-Sealer) in roots, filled with thermo-plasticized injectable technique aided by Calamus-Flow-Delivery-System, on bond strength to radicular dentin, in comparison with conventional epoxy-resin-based sealer (AH-Plus) along with cold-lateral-compaction technique. Root canals of mandibular-premolar teeth (n = 80) were instrumented using Protaper Universal rotary files and were randomly divided into four experimental groups (n = 20) as follows: (1) AH-Plus + cold-lateral-compaction technique; (2) Endosequence-BC-Sealer + cold-lateral-compaction technique; (3) AH-Plus + thermo-plasticized injectable technique; and (4) Endosequence-BC-Sealer + thermo-plasticized injectable technique. Horizontal disc shaped samples from each group (n = 60/group) were obtained and push-out bond strength testing was performed at a cross-head speed of 0.5 mm/min. Data were analyzed statistically using nonparametric Kruskal-Wallis analysis and Mann-Whitney test (p < 0.001). The statistical analysis revealed a significant difference amongst the groups (p < 0.001). The highest bond strength values were found in group 1 compared with all the other experimental groups (p < 0.001), whereas the lowest bond strength values were found in group 4 (p < 0.001). It was concluded that thermo-plasticized injectable technique with Calamus-Flow-Delivery-System lowered the bond strengths of the sealers, especially Endosequence-BC-Sealer. Therefore, this technique is not recommended to calcium-silicate-based sealers. Further studies are needed to confirm the findings of this study.
|
|---|