Preparation of a Fast Water-Based UV Cured Polyurethane-Acrylate Wood Coating and the Effect of Coating Amount on the Surface Properties of Oak (<i>Quercus alba</i> L.)

A fast water-based ultraviolet light (UV) curing polyurethane-acrylate (PUA) wood coating was prepared in the laboratory, and applied on oak (<i>Quercus alba</i> L.) at different coating amounts. The PUA wood coating can be fast cured within 22 min, which highly improved the drying speed...

Full description

Bibliographic Details
Main Authors: Jin Wang, Huagui Wu, Ru Liu, Ling Long, Jianfeng Xu, Minggui Chen, Hongyun Qiu
Format: Article
Language:English
Published: MDPI AG 2019-08-01
Series:Polymers
Subjects:
Online Access:https://www.mdpi.com/2073-4360/11/9/1414
Description
Summary:A fast water-based ultraviolet light (UV) curing polyurethane-acrylate (PUA) wood coating was prepared in the laboratory, and applied on oak (<i>Quercus alba</i> L.) at different coating amounts. The PUA wood coating can be fast cured within 22 min, which highly improved the drying speed compared to normal water-based wood coatings (often higher than 35 min). The coating amounts affected the coating properties after curing on oak. With the increase of coating amount, the adhesion, hardness and gloss value of surface increased to different extents. Meanwhile, the surface of sample became smooth gradually because the voids of the oak were filled. Thus, higher coating amount resulted in better coating properties. However, no significant increase of penetration depth was found. During curing, the hydroxyl groups of the wood reacted with the coating. The optimal parameter in this study was the coating amount of 120 g/m<sup>2</sup>, where the adhesion reached 1 (with 0&#8722;5% cross-cut area of flaking along the edges), with the hardness of 2H and the gloss of 92.56&#176;, which met the requirement of Chinese standard GB/T 18103&#8722;2013, and could be used for engineered wood flooring.
ISSN:2073-4360