| Summary: | Adhesive is the key component and factor for the manufacture of glulam, affected both the properties and cost of glulam product. Bio-based resorcinol-phenol-formaldehyde (BRPF) resin was developed by partly replacing the expensive resorcinol and phenol with the cheap biomass derived pyrolysis oil. The press process parameters and the dosage of adhesive and corresponding curing agent were selected as the factors and extensively studied. BRPF resin was successfully used to bond the laminas to produce glulam, and the optimized process parameters for the cold-pressing adhesion of BRPF resin with pine wood were obtained as follows: the cold-pressing pressure 1.4 MPa, the cold-pressing time 9 h, the amount of adhesive coating 320 g/m2, and the proportion of curing agent (poly-formaldehyde) 17%. The mechanical performances of laminated wood bonding with BRPF resin under the optimal condition were further verified. It is believed that the results obtained here will promote the use of bio-based resin in the bonding of laminated wood, and then contribute to the green manufacturing of glulam with lower cost.
|
|---|