Hydrogen-assisted fatigue crack propagation in a pure BCC iron. Part I: Intergranular crack propagation at relatively low stress intensities
The role of hydrogen on intergranular (IG) fracture in hydrogen-assisted fatigue crack growth (HAFCG) of a pure iron at low stress intensity was discussed in terms of the microscopic deformation structures near crack propagation paths. The main cause of IG fracture was assumed to be the hydrogen-enh...