Evolution of Secondary α Phase during Aging Treatment in Novel near β Ti-6Mo-5V-3Al-2Fe Alloy
Evolution of secondary α phase during aging treatment of a novel near β titanium alloy Ti-6Mo-5V-3Al-2Fe(wt.%) was studied by OM, SEM, and TEM. Results indicated that size and distribution of secondary α phase were strongly affected by aging temperature and time. Athermal...