| Summary: | In this research, experiments were carried out to investigate the effects of operating parameters onthe pervaporation performance for the separation of ethanol-water solutions. Composite silicone membranessupported on polysulfone prepared with varied silicone contents and commercial polyvinyl alcohol (Pervap®2211, Sulzer) membranes were used. The results showed that the composite silicone/polysulfone membranescoated with 3 wt% of silicone exhibited highest permeation flux with slightly lower separation factor forethanol. Furthermore, it was found that the composite silicone/polysulfone membranes were suitable for theseparation of ethanol from a dilute ethanol solutions. Both the separation factor and permeation flux of the composite membranes increased with increasing temperature and feed concentration. A membrane coated with a 7 wt% silicone gave highest separation factor of 7.32 and permeation flux of 0.44 kg/m2h at 5 wt% ethanol feed concentration and feed temperature of 70ºC. For polyvinyl alcohol membranes, the results showed that the membranes were suitable for the dehydration of concentrated ethanol solutions. The permeation flux increased and the separation factor for water decreased with increasing water feed concentration and temperature. The membrane gave highest separation factor of 248 and permeation flux of 0.02 kg/m2h at 5 wt% water feed concentration and feed temperature of 30ºC.
|
|---|