Development and Bone Regeneration Capacity of Premixed Magnesium Phosphate Cement Pastes

• Main Authors: Andrea Ewald, Dorothea Kreczy, Theresa Brückner, Uwe Gbureck, Melanie Bengel, Andreas Hoess, Berthold Nies, Julia Bator, Uwe Klammert, Andreas Fuchs
• Format: Article
• Language: English
• Published: MDPI AG 2019-07-01
• Series: Materials
• Subjects: magnesium phosphate cement; prefabricated paste; implantation
• Online Access: https://www.mdpi.com/1996-1944/12/13/2119
• ISSN: 1996-1944

Magnesium phosphate cements (MPC) have been demonstrated to have a superior bone regeneration capacity due to their good solubility under in vivo conditions. While in the past only aqueous MPC pastes have been applied, the current study describes the fabrication and in vitro/in vivo testing of an oil-based calcium doped magnesium phosphate (CaMgP) cement paste. Premixed oil-based pastes with CaMgP chemistry combine the advantages of conventional MPC such as high mechanical strength and good resorbability with a prolonged shelf-life and an easier clinical handling. The pastes set in an aqueous environment and predominantly form struvite and achieve a compressive strength of ~8−10 MPa after setting. The implantation into a drill-hole defect at the distal femoral condyle of New Zealand white rabbits over a course of 6 and 12 weeks demonstrated good biocompatibility of the materials without the formation of soft connective tissue or any signs of inflammation. In contrast to a hydroxyapatite forming reference paste, the premixed CaMgP pastes showed subsequent degradation and bony regeneration. The CaMgP cement pastes presented herein are promising bone replacement materials with excellent material properties for an improved and facilitated clinical application.