Au/Cu2Te/CdTe/CdS/TCO/Glass Solar Cells with CdIn2O4 Obtained by Sol-Gel as TCO
An Au/Cu2Te/CdTe/CdS/TCO/glass heterostructure based superstrate solar cells with 2.5 mm2 of area, where the CdTe layer was prepared by means of closed spaced sublimation (CSS) and the CdS by chemical bath, reached an efficiency η value of 12.1%. As transparent conductive oxide (TCO), a thin film of...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Limited
2014-01-01
|
| Series: | International Journal of Photoenergy |
| Online Access: | http://dx.doi.org/10.1155/2014/920785 |
| Summary: | An Au/Cu2Te/CdTe/CdS/TCO/glass heterostructure based superstrate solar cells with 2.5 mm2 of area, where the CdTe layer was prepared by means of closed spaced sublimation (CSS) and the CdS by chemical bath, reached an efficiency η value of 12.1%. As transparent conductive oxide (TCO), a thin film of cadmium-indium oxide (CdIn2O4:CIO), obtained by sol-gel technique, was used. A systematic optimization of the thermal activation of the CdTe/CdS/CIO central part of the device with a CdCl2 vapor ambient made the conversion efficiency of the Au/Cu2Te/CdTe/CdS/CIO/glass heterostructure reaches 9.94% for the CdTe layer with thickness of 1.8 μm. This efficiency was reached only through an open circuit voltage VOC optimization. A maximum η of 12.1% was reached with the established procedure of optimization and when the CdTe layer thickness was increased to 3.1 ± 0.05 μm. The substitution of CIO by commercial ITO provoked in the cell a decrease of η from 12.1% to 7.2%, both devices prepared under the same conditions. Starting from these results, we can say that CIO was a better TCO than commercial ITO in our solar cell, with the advantage that CIO was obtained by sol-gel, which is a simple and economical technique. |
|---|---|
| ISSN: | 1110-662X 1687-529X |