Investigation on the microstructural evolution and precipitation hardening mechanism of 1Cr15Ni36W3Ti superalloy with varied C contents
Impacts of C content on the microstructural evolution and precipitation hardening mechanism in 1Cr15Ni36W3Ti was studied by phase modelling, microstructural analysis and room-temperature tensile test. The casting material was composed of γ, interdendritic primary MC and secondary MC carbides. The mo...