Effect of Annealing on the Microstructure and SERS Performance of Mo-48.2% Ag Films
Mo-48.2% Ag films were fabricated by direct current (DC) magnetron sputtering and annealed in an argon atmosphere. The effects of annealing on the surface morphology, resistivity and surface-enhanced Raman scattering (SERS) performance of Mo-48.2% Ag films were investigated. Results show a mass of p...