| Summary: | The effect of different In contents on the melting characteristics, mechanical properties, and microstructure of 12Ag–Cu–Zn–Sn filler metal was investigated in this paper, and flame brazing of 304 stainless steel and copper plates was done using the 12Ag–Cu–Zn–Sn–<i>x</i>In filler metal. The results indicate that adding appropriate amount of In can evidently decrease the solidus and liquidus temperatures and improve the wettability of the low silver based filler metals. In addition, the shear strength of 304 stainless steel and copper plates joint brazed by 12Ag–Cu–Zn–Sn–1In are satisfactory due to the solution strength effect, and scanning electron microscopy examination of the braze-zone revealed that more relatively sound joints were obtained when brazing was done with 12Ag–Cu–Zn–Sn–<i>x</i>In filler metal than with Indium free one; its performance is comparable to that of the joint brazed with the 20Ag–Cu–Zn–Sn filler metal, having a remarkable silver-saving effect.
|
|---|