Influence of fading on characteristics of thermal analysis curve of compacted graphite iron

• Main Authors: Liu Jinhai, Yi Litao, Li Guolu
• Format: Article
• Language: English
• Published: Foundry Journal Agency 2011-08-01
• Series: China Foundry
• Subjects: compacted graphite iron; thermal analysis; fading; compacted graphite percentage; characteristic value
• Online Access: http://www.foundryworld.com/uploadfile/2011083135382569.pdf

In general, during the production of compacted graphite iron (CGI), the active residual magnesium reduces and the effect of inoculation fades after magnesium treatment. In this paper, characteristics of the thermal analysis curve of CGI are compared with those of ductile iron and grey cast iron. The fading effect on the compacted graphite percentage and thermal analysis curve were also studied. Results indicate that the undercooling of CGI is as low as that of ductile iron, but CGI shows evident recalescence. In fading process, the magnesium element acts with oxygen. For a decrease in magnesium content, both the compacted graphite percentage and the austenitic liquidus temperature increase. The temperature of eutectic undercooling (TEU) decreases before the flake graphite appears. After that, TEU increases quickly, up to as high as 20℃, and then gradually decreases. The evolution of recalescence degree is opposite to that of TEU.