| Summary: | The interfacial bond between cement concrete base plate (CCBP) and asphalt concrete waterproofing layer (ACWL) is a weak portion in the newly developed Chinese high-speed railway ballastless track. The interface damage caused due to fluctuating temperature load and dynamic train load is one of the most critical problems in Northern China. This paper aims to investigate the interface damage evolution process under temperature load via experimental and simulation analysis. Full-scale transverse shear tests were performed to explore the interface bond-slip mode of the adjacent ACWL and CCBP. Then, a finite element model of a ballastless track structure was built and a cohesive zone model (CZM) was utilized to model the interface damage initiation, crack propagation, and delamination process under uniform/gradient temperature load. Furthermore, the dynamic response of the ballastless track where CCBP and ACWL were partly/totally debonded was investigated and compared with the perfectly bonded structure. The results demonstrate that bilinear CZM is capable of revealing the interface damage initiation, crack propagation, and delamination process under temperature load. The interface state between the adjacent CCBP and ACWL was greatly affected by temperature changes and the interface bonding state had a great impact on the dynamic response of ballastless track.
|
|---|