Effect of nonmetallic inclusions on steel welds metal hot cracking
Intercrystally distributed nonmetallic inclusions greatly increase weld susceptibility to hot cracking. Oxide and sulphide inclusions are the result of contaminated base material or its highly oxidised surfaces and they can be a consequence of metallurgical reactions between welding slag and remelte...
Main Authors: | , , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Croatian Metallurgical Society
2014-04-01
|
Series: | Metalurgija |
Subjects: | |
Online Access: | http://hrcak.srce.hr/file/162229 |
Summary: | Intercrystally distributed nonmetallic inclusions greatly increase weld susceptibility to hot cracking. Oxide and sulphide inclusions are the result of contaminated base material or its highly oxidised surfaces and they can be a consequence of metallurgical reactions between welding slag and remelted base material, while carbide inclusions can occur due to the mixing of high-carbon base and low-carbon filler material. All welding surfaces must thus be cleaned before welding and the least possible mixture of base with filler material must be enusured during welding. |
---|---|
ISSN: | 0543-5846 1334-2576 |