| Summary: | The mill scale is a waste from the iron and steel industry. Due to the high content of iron in the form of oxides, it is an attractive material for the recovery of metallic iron by reduction. The product of mill scale reduction is an iron with a very extended surface and a high affinity for oxygen. The smaller iron particles are, the easier it is for spontaneous rapid oxidation, which can be linked to pyrophoricity. This article presents results of experiments using the TG/DTA thermal analysis method aimed at verifying the possibility of recovering iron from the mill scale by a reduction with carbon monoxide at 850 °C, 950 °C, and 1050 °C, taking into account the phenomenon of secondary oxidation in contact with oxygen from air at temperatures of 300 °C, 350 °C, and 400 °C. Two forms of mill scale were used for tests, in the original state and after grinding to develop the surface.
|
|---|