| Summary: | In order to fabricate the abrasive wheels with good grain self-sharpening capacity, two types of multicrystalline CBN grains, that is, polycrystalline CBN (PCBN) and binderless CBN (BCBN), were brazed using Cu-Sn-Ti alloy, respectively. Comparative investigation on the brazing interface, compressive strength, and wear properties of the different grains was carried out. Results obtained show that the PCBN grains have more intricate reaction, more complicated resultants, and thicker reaction layer than the BCBN counterparts under the identical brazing conditions. Though the average compressive strength of the PCBN grains is similar to that of BCBN ones, stronger self-sharpening action by virtue of the microfracture behavior takes place with BCBN grains during grinding. As a consequence, compared to the brazed PCBN wheels and the conventional monocrystalline CBN (MCBN) ones, longer service life is obtained for the brazed BCBN wheels.
|
|---|