| Summary: | The stability of barium zirconate (BaZrO3) components in reducing conditions at high temperatures has been studied. The experiments consisted in thermal treatments at temperatures in the range 1300°C-1500°C, for times up to 5 hours, under vacuum (absolute pressure: 10 Pa). Weight losses up to 3% have been achieved. XRD and SEM characterization of the ceramics after the above experiments showed the presence of high aspect-ratio monoclinic zirconia particles on the surfaces of the ceramics. These results can be explained in terms of selective volatilization of BaO, and must be considered for using barium zirconate ceramics at high temperatures under reducing environments.<br><br>Las cerámicas de circonato de bario (BaZrO3) se descomponen por tratamiento térmico en condiciones reductoras en vacío. Esta descomposición se produce por volatilización selectiva del BaO, y conduce a la aparición de partículas de circona monoclínica de elevada relación de aspecto en las superficies del material expuestas a la atmósfera reductora. La profundidad del ataque superficial y las pérdidas de peso aumentan con el tiempo y la temperatura del tratamiento. Esta inestabilidad condiciona el uso de materiales de BaZrO3 en condiciones fuertemente reductoras a altas temperaturas.
|
|---|