Fatigue Life Prediction in Journal Bearing
Failure of fatigue is damaged materials where caused frequent load. Fatigue owing to some factors, which is Stress concentration on fatigue, Stress life, Effect size and surface, and Change properties of surface. The fatigue failure of a material is dependent on the interaction of a large stress wit...
| Main Authors: | , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hasanuddin University
2017-03-01
|
| Series: | International Journal on Smart Material and Mechatronics |
| Subjects: | |
| Online Access: | http://eng.unhas.ac.id/ijsmm/index.php/ijsmm/article/view/29 |
| Summary: | Failure of fatigue is damaged materials where caused frequent load. Fatigue owing to some factors, which is Stress concentration on fatigue, Stress life, Effect size and surface, and Change properties of surface. The fatigue failure of a material is dependent on the interaction of a large stress with a critical flow. In essence, fatigue is controlled by the weakest link of the material, with the probability of a weak link increasing with material volume. This phenomenon is evident in the fatigue test results of a material using specimens of varying diameters. From this research we can get effect of concentration stress on strength fatigue with S-N method. On this method only count fatigue life or endurance limit from Journal bearing housing. By Finite Element Analysis, it is not so easy to determine fatigue life. When we find the first yield point, it means this point is in the highest stress state. Then we can refer S-N curve. In this paper, the effect of bearing and housing elasticity on the stress field, which could result in surface fatigue in journal bearing, has been investigated. This condition is proved with occurred slip lines on surface of specimen. These slip lines are caused on some thousands stress cycles. Additional crack is happened immediately and finally long enough crack. So that formed unstable crack that caused fracture of brittleness or fracture of toughness because section of specimen cannot keep |
|---|---|
| ISSN: | 2356-5314 2460-075X |