Effect of growth rate on microstructure and microhardness of directionally solidified Ti-44Al-5Nb-1.5Cr-1.5Zr-1Mo-0.1B alloy
The effect of growth rates (V=2–50 µm·s−1) on microstructure and microhardness of directionally solidified Ti-44Al-5Nb-1.5Cr-1.5Zr-1Mo-0.1B (at.%) alloy at a constant temperature gradient (G=18 K-mm−1) was investigated. Results indicated that β phase was the primary phase of the directionally solidi...