Influence of Welding Speed on Fracture Toughness of Friction Stir Welded AA2024-T351 Joints

• Main Authors: Miodrag Milčić, Dragan Milčić, Tomaž Vuherer, Ljubica Radović, Igor Radisavljević, Aleksija Đurić
• Format: Article
• Language: English
• Published: MDPI AG 2021-03-01
• Series: Materials
• Subjects: friction stir welding; process parameters; welding speed; tool rotation speed; AA-2024-T351; fracture toughness
• Online Access: https://www.mdpi.com/1996-1944/14/6/1561

In order to ensure a quality welded joint, and thus safe operation and high reliability of the welded part or structure achieved by friction stir welding, it is necessary to select the optimal welding parameters. The parameters of friction stir welding significantly affect the structure of the welded joint, and thus the mechanical properties of the welded joint. Investigation of the influence of friction stir welding parameters was performed on 6-mm thick plates of aluminum alloy AA2024 T351. The quality of the welded joint is predominantly influenced by the tool rotation speed <i>n</i> and the welding speed v. In this research, constant tool rotation speed was adopted <i>n</i> = 750 rpm, and the welding speed was varied (<i>v</i> = 73, 116 and 150 mm/min). By the visual method and radiographic examination, imperfections of the face and roots of the welded specimens were not found. This paper presents the performed experimental tests of the macro and microstructure of welded joints, followed by tests of micro hardness and fracture behavior of Friction Stir Welded AA2024-T351 joints. It can be concluded that the welding speed of <i>v</i> = 116 mm/min is favorable with regard to the fracture behavior of the analysed FSW-joint.