Effect of thermal aging on the mechanical, intergranular corrosion and corrosion fatigue properties of Z3CN20.09M cast duplex stainless steel
The effect of thermal aging at 475 °C and 750 °C of Z3CN20.09M cast duplex stainless steel (CDSS) on microstructure, mechanical and intergranular corrosion properties were investigated by transmission electron microscope (TEM), nano indenter, scanning electron microscope (SEM) and corrosion fatigue...
Main Authors: | , , , , , , |
---|---|
Format: | Article |
Language: | English |
Published: |
Elsevier
2021-08-01
|
Series: | Nuclear Engineering and Technology |
Subjects: | |
Online Access: | http://www.sciencedirect.com/science/article/pii/S1738573321000632 |
id |
doaj-8ded3033c2054fad9bc8d855b69b73e0 |
---|---|
record_format |
Article |
spelling |
doaj-8ded3033c2054fad9bc8d855b69b73e02021-07-03T04:44:51ZengElsevierNuclear Engineering and Technology1738-57332021-08-0153825912599Effect of thermal aging on the mechanical, intergranular corrosion and corrosion fatigue properties of Z3CN20.09M cast duplex stainless steelWenxin Ti0Huanchun Wu1Fei Xue2Guodong Zhang3Qunjia Peng4Kewei Fang5Xitao Wang6Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing, 100083, China; Plant Life Management Center, Suzhou Nuclear Power Research Institute, Suzhou, 215004, ChinaPlant Life Management Center, Suzhou Nuclear Power Research Institute, Suzhou, 215004, China; Corresponding author.Plant Life Management Center, Suzhou Nuclear Power Research Institute, Suzhou, 215004, ChinaPlant Life Management Center, Suzhou Nuclear Power Research Institute, Suzhou, 215004, ChinaPlant Life Management Center, Suzhou Nuclear Power Research Institute, Suzhou, 215004, ChinaPlant Life Management Center, Suzhou Nuclear Power Research Institute, Suzhou, 215004, ChinaCollaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing, 100083, China; Corresponding author.The effect of thermal aging at 475 °C and 750 °C of Z3CN20.09M cast duplex stainless steel (CDSS) on microstructure, mechanical and intergranular corrosion properties were investigated by transmission electron microscope (TEM), nano indenter, scanning electron microscope (SEM) and corrosion fatigue test system. The result indicated that the spinodal decomposition and G precipitated were occurred after aged at 475 °C, as well as sigma precipitated at 750 °C. The microstructure degeneration of ferrite was saturated after aged for 2000h and 200 h at 475 °C and 750 °C respectively. The mechanical properties, intergranular corrosion resistance and corrosion fatigue lives were continuing deteriorated with increasing the aging time at both temperatures. The difference of the degeneration mechanisms of Z3CN20.09M CDSS aged at 475 °C and 750 °C was analyzed.http://www.sciencedirect.com/science/article/pii/S1738573321000632Thermal agingSpinodal decompositionSigma precipitationCorrosion fatigueHigh temperature water |
collection |
DOAJ |
language |
English |
format |
Article |
sources |
DOAJ |
author |
Wenxin Ti Huanchun Wu Fei Xue Guodong Zhang Qunjia Peng Kewei Fang Xitao Wang |
spellingShingle |
Wenxin Ti Huanchun Wu Fei Xue Guodong Zhang Qunjia Peng Kewei Fang Xitao Wang Effect of thermal aging on the mechanical, intergranular corrosion and corrosion fatigue properties of Z3CN20.09M cast duplex stainless steel Nuclear Engineering and Technology Thermal aging Spinodal decomposition Sigma precipitation Corrosion fatigue High temperature water |
author_facet |
Wenxin Ti Huanchun Wu Fei Xue Guodong Zhang Qunjia Peng Kewei Fang Xitao Wang |
author_sort |
Wenxin Ti |
title |
Effect of thermal aging on the mechanical, intergranular corrosion and corrosion fatigue properties of Z3CN20.09M cast duplex stainless steel |
title_short |
Effect of thermal aging on the mechanical, intergranular corrosion and corrosion fatigue properties of Z3CN20.09M cast duplex stainless steel |
title_full |
Effect of thermal aging on the mechanical, intergranular corrosion and corrosion fatigue properties of Z3CN20.09M cast duplex stainless steel |
title_fullStr |
Effect of thermal aging on the mechanical, intergranular corrosion and corrosion fatigue properties of Z3CN20.09M cast duplex stainless steel |
title_full_unstemmed |
Effect of thermal aging on the mechanical, intergranular corrosion and corrosion fatigue properties of Z3CN20.09M cast duplex stainless steel |
title_sort |
effect of thermal aging on the mechanical, intergranular corrosion and corrosion fatigue properties of z3cn20.09m cast duplex stainless steel |
publisher |
Elsevier |
series |
Nuclear Engineering and Technology |
issn |
1738-5733 |
publishDate |
2021-08-01 |
description |
The effect of thermal aging at 475 °C and 750 °C of Z3CN20.09M cast duplex stainless steel (CDSS) on microstructure, mechanical and intergranular corrosion properties were investigated by transmission electron microscope (TEM), nano indenter, scanning electron microscope (SEM) and corrosion fatigue test system. The result indicated that the spinodal decomposition and G precipitated were occurred after aged at 475 °C, as well as sigma precipitated at 750 °C. The microstructure degeneration of ferrite was saturated after aged for 2000h and 200 h at 475 °C and 750 °C respectively. The mechanical properties, intergranular corrosion resistance and corrosion fatigue lives were continuing deteriorated with increasing the aging time at both temperatures. The difference of the degeneration mechanisms of Z3CN20.09M CDSS aged at 475 °C and 750 °C was analyzed. |
topic |
Thermal aging Spinodal decomposition Sigma precipitation Corrosion fatigue High temperature water |
url |
http://www.sciencedirect.com/science/article/pii/S1738573321000632 |
work_keys_str_mv |
AT wenxinti effectofthermalagingonthemechanicalintergranularcorrosionandcorrosionfatiguepropertiesofz3cn2009mcastduplexstainlesssteel AT huanchunwu effectofthermalagingonthemechanicalintergranularcorrosionandcorrosionfatiguepropertiesofz3cn2009mcastduplexstainlesssteel AT feixue effectofthermalagingonthemechanicalintergranularcorrosionandcorrosionfatiguepropertiesofz3cn2009mcastduplexstainlesssteel AT guodongzhang effectofthermalagingonthemechanicalintergranularcorrosionandcorrosionfatiguepropertiesofz3cn2009mcastduplexstainlesssteel AT qunjiapeng effectofthermalagingonthemechanicalintergranularcorrosionandcorrosionfatiguepropertiesofz3cn2009mcastduplexstainlesssteel AT keweifang effectofthermalagingonthemechanicalintergranularcorrosionandcorrosionfatiguepropertiesofz3cn2009mcastduplexstainlesssteel AT xitaowang effectofthermalagingonthemechanicalintergranularcorrosionandcorrosionfatiguepropertiesofz3cn2009mcastduplexstainlesssteel |
_version_ |
1721321303157243904 |