Effect of TiO2 Photoanode Porosity on Dye Diffusion Kinetics and Performance of Standard Dye-Sensitized Solar Cells

• Main Authors: Cecile Charbonneau, Theo Tanner, Matthew L. Davies, Trystan M. Watson, David A. Worsley
• Format: Article
• Language: English
• Published: Hindawi Limited 2016-01-01
• Series: Journal of Nanomaterials
• Online Access: http://dx.doi.org/10.1155/2016/9324858

Low-cost water-based P25-TiO2 pastes were formulated and used to produce porous TiO2 films in application to the fabrication of dye-sensitized solar cells. The structural properties of the films were characterized using a variety of techniques such as stylus profilometry, FEG-SEM imaging, BET surface area, and BJH pore size analyses. These were compared to films produced from a commercial paste, DSL 18 NR-AO (Dyesol). The major difference was in the fraction of macroporosity: 23% of the total pore volume for films produced with the commercial material and 67–73% for the P25-TiO2 films owing to the vast difference in dispersion and size distribution of the particles in the two types of pastes. The macroporosity was found to have a dramatic effect on the dye diffusion kinetics measured using in situ UV-Vis reflectance spectroscopy. The sensitization of P25-based films was much faster for heavily macroporous P25-TiO2 films (>90% saturation at 15–35 mins) than for their commercial analogue (>90% saturation at 110 mins). DSC devices built with optimized P25-TiO2 photoanodes showed better performance at short dye immersion time (30 mins and 1 hr) due to faster percolation of the dye molecules through the film.