High-Temperature Mechanical Behaviors of SiO<sub>2</sub>-Based Ceramic Core for Directional Solidification of Turbine Blades

The high-temperature mechanical behaviors of SiO<sub>2</sub>-based ceramic cores for the directional solidification of turbine hollow blades were investigated. Isothermal uniaxial compression tests of ceramic core samples were conducted on a Gleeble-1500D mechanical simulator with an inn...

Full description

Bibliographic Details
Main Authors: Jiangwei Zhong, Qingyan Xu
Format: Article
Language:English
Published: MDPI AG 2020-10-01
Series:Materials
Subjects:
Online Access:https://www.mdpi.com/1996-1944/13/20/4579
Description
Summary:The high-temperature mechanical behaviors of SiO<sub>2</sub>-based ceramic cores for the directional solidification of turbine hollow blades were investigated. Isothermal uniaxial compression tests of ceramic core samples were conducted on a Gleeble-1500D mechanical simulator with an innovative auxiliary thermal system. The stress–strain results and macro- and micro- structures of SiO<sub>2</sub>-based ceramic cores were investigated experimentally. The microstructures were characterized by the scanning electron microscope (SEM). Based on the experimental data, a nonlinear constitutive model for high temperature compressive damage was established. The statistical results of Weibull moduli show that the stability of hot deformation increases with the increase of temperature. The fracture type of the SiO<sub>2</sub>-based core samples is brittle fracture, but when the temperature exceeds 1400 °C, the mechanical behavior exhibits thermo-viscoelastic and viscoplastic property. Under high-temperature (>1400 °C) and stress conditions, the strength of the ceramic core is weakened owing to the viscous slip of SiO<sub>2</sub>, which is initially melted at the temperature of 1400 °C. The comparison results between the predictions of nonlinear model and experimental values indicate that the model is applicable.
ISSN:1996-1944