Enhanced wear resistance of engineered glass-ceramic by nanostructured self-lubrication
A new kind of micro-nanostructured glass-ceramic based on albite and anorthite crystallizations, >90%, has been obtained following a fast sintering processing route. Flexural strength values up to 111 MPa and microhardness values of 9.5 GPa are measured, supposing an improvement of ~60% regarding...