Effect of Intermediate Annealing on Microstructure and Property of 5182 Aluminum Alloy Sheet for Automobile

• Main Authors: WANG Yu, CAO Ling-yong, LI Jun-peng, ZHANG Hua, GUO Fu-an
• Format: Article
• Language: zho
• Published: Journal of Materials Engineering 2016-09-01
• Series: Journal of Materials Engineering
• Subjects: intermediate annealing; aluminium alloy; microstructure; mechanical property; forming ability
• Online Access: http://jme.biam.ac.cn/CN/10.11868/j.issn.1001-4381.2016.09.012

Effect of intermediate annealing on the microstructure and properties of 5182 aluminum alloy sheet with full annealed state (5182-O) was investigated by means of optical microscope, scanning electron microscope and universal testing machine. The results indicate that compared with 5182-O sheet without intermediate annealing, 5182-O sheet with intermediate annealing possesses too fine grain size, intermetallic compounds not broken enough, larger size intermetallic particles, less dispersed phase. Yield strength and ultimate tensile strength, work hardening exponent and normal anisotropy of plastic strain ratio decrease but planner anisotropy of plastic strain ratio increases. The mechanical properties and forming ability of 5182-O aluminum alloy sheet and its microstructure are not improved significantly after intermediate annealing.