| Summary: | The objective of this work was to investigate the effect of two different sintering additives (CeO2 and Y2O3 + Al2O3), sintering time and amount of b-Si3N4 seeds on the densification, mechanical properties and microstructure of self-reinforced Si3N4 based composites obtained by pressureless sintering. Preparation of b-Si3N4 seeds, also obtained by a pressureless sintering procedure, is described. Samples without seeds were prepared for comparison. The results imply that self-reinforced silicon nitride based composites with densities close to the theoretical values and with fracture toughness of 9.3 MPa m1/2 can be obtained using a presureless sintering procedure.
|
|---|