Strength and Ductility Improvement through Thermomechanical Treatment of Wire-Feed Electron Beam Additive Manufactured Low Stacking Fault Energy (SFE) Aluminum Bronze
An as-cast macrostructure of electron beam additively manufactured metallic materials was represented by coarse columnar grains whose axes were inclined at 25° with respect to the substrate’s plane. One part of the as-grown samples was annealed to form a coarse grain microstructure while the other p...