Effect of Complex Organo-Mineral Modifier on the Properties of Corrosion-Resistant Concrete

• Main Authors: Van Tang Lam, Xuan Ngo Hung, Vu Kim Dien, Bulgakov Boris, Aleksandrova Olga
• Format: Article
• Language: English
• Published: EDP Sciences 2018-01-01
• Series: MATEC Web of Conferences
• Online Access: https://doi.org/10.1051/matecconf/201825101005

This paper reports the results of a research study aimed at identifying the compositional features of fly ash (FA) TPP “Pha Lai” (Vietnam), silica fume SF-90 (SF90) and superplasticizer SilkRoad SR 5000F (SR5000) contents that influence the sulfate resistance of corrosion-resistant concrete. The effect of FA, SF90 and SR5000 on the strength of corrosion-resistant concrete is obtained quickly, high early-strength concrete. In details, the compressive strength at the age of 1 and 3 days are respectively 29.6% and 61.13% in comparison to 28 days period. The deformation of corrosion-resistant concrete prisms in 5% sodium sulfate solution after 28 days of testing were determined by Russian standard GOST P 56687-2015. Using the mathematical planning method for four factors and the Matlab computer programs was obtained the mathematical model, which was adequately described the influence ofthe water-binding ratio, FA, SF90 and SR5000 contents on the concrete deformation. It was also noted that the effect of FA content is more pronounced than the water-binding ratio and content SF90. In addition, the effect of SR5000 content on the deformation of concrete is negligible, so it was discarded.