The Analysis of the High Speed Wire Drawing Process of High Carbon Steel Wires Under Hydrodynamic Lubrication Conditions
In this work the analysis of the wire drawing process in hydrodynamic dies has been done. The drawing process of φ5.5 mm wire rod to the final wire of φ1.7 mm was conducted in 12 passes, in drawing speed range of 5-25 m/s. For final wires of φ1.7 mm the investigation of topography of wire surface, t...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Polish Academy of Sciences
2015-04-01
|
| Series: | Archives of Metallurgy and Materials |
| Subjects: | |
| Online Access: | http://www.degruyter.com/view/j/amm.2015.60.issue-1/amm-2015-0066/amm-2015-0066.xml?format=INT |
| Summary: | In this work the analysis of the wire drawing process in hydrodynamic dies has been done. The drawing process of φ5.5 mm wire rod to the final wire of φ1.7 mm was conducted in 12 passes, in drawing speed range of 5-25 m/s. For final wires of φ1.7 mm the investigation of topography of wire surface, the amount of lubricant on the wire surface and the pressure of lubricant in hydrodynamic dies were determined. Additionally, in the work selected mechanical properties of the wires have been estimated. |
|---|---|
| ISSN: | 2300-1909 |