Research Progress in Cemented Carbide with Co-Ni-Al Composite Binder Phase

• Main Authors: LONG Jianzhan, DU Yong, LU Bizhi, ZHANG Weibing, XU Tao, ZHANG Zhongjian, YI Maozhong
• Format: Article
• Language: zho
• Published: Journal of Aeronautical Materials 2018-10-01
• Series: Journal of Aeronautical Materials
• Subjects: Co-Ni-Al composite binder phase; cemented carbide; ordered phase precipitation; integrated computational material engineering
• Online Access: http://jam.biam.ac.cn/CN/Y2018/V38/I5/47

The application background of Co-Ni-Al composite binder phase in cemented carbide was introduced. The latest research results of Co-based superalloy and the properties of cemented carbide with binder strengthened by ordered phase were briefly described. The application of integrated computational material engineering in the research and development of Co-Ni-Al composite binder was introduced. The progress in the preparation, microstructure characterization and performance of WC-Co-Ni-Al cemented carbides were summarized. The results show that the composition of Co-Ni-Al composite binder has obvious influence on the solid-liquid interface energy and the liquid-phase nucleation driving force of the alloy. Accordingly, the grain size of the binder phase and the grain morphology of WC are affected. Ultimately these factors affect the performance of the alloy. It is pointed out that the performance of cemented carbide strengthened by ordered γ′ phase precipitation can be improved significantly. It is expected to obtain high-performance cemented carbide materials with excellent high-temperature resistance, corrosion resistance and oxidation resistance. It is proposed that the interfacial microstructure, the relationship between C content and precipitation phase and the anti-wear mechanism of cemented carbide with Co-Ni-Al composite binder phase should be emphasized in future.