Effect of Meltable Triazine-DOPO Additive on Rheological, Mechanical, and Flammability Properties of PA6

• Main Authors: Irina Butnaru, María P. Fernández-Ronco, Justyna Czech-Polak, Maciej Heneczkowski, Maria Bruma, Sabyasachi Gaan
• Format: Article
• Language: English
• Published: MDPI AG 2015-08-01
• Series: Polymers
• Subjects: Polyamide 6; halogen-free flame retardant; flame retardancy; PCFC; UL-94 test; DIP-MS
• Online Access: http://www.mdpi.com/2073-4360/7/8/1469

Through a straightforward approach, a new meltable, halogen-free, nitrogen-phosphorus-based flame retardant (FR), 6-(2-(4,6-diamino-1,3,5-triazin-2-yl)ethyl) dibenzo[c,e][1,2]oxaphosphinine 6-oxide (DTE-DOPO) was synthesized and incorporated in polyamide 6 (PA6). It was proved that a very low phosphorus content of 1.46 wt% for DTE-DOPO additive improved the flame retardancy of PA6, leading to a non-flammable material. The performance of the new additive was compared to that of the commercially-available Exolit® OP 1230. The PA6 formulations were evaluated by measuring the rheological, mechanical, and flammability behavior. Using compounding by melt extrusion, 17 wt% additives was introduced into PA6 matrix and the corresponding formulations were characterized. The results evidenced a higher homogeneity of DTE-DOPO with PA6, a high thermal stability with a catalyzing decomposition effect on PA6 caused by the presence of the new developed FR, enhanced elasticity for the PA6/DTE-DOPO formulation and a V0 rating for both formulations. Thermal and fire analysis indicated a primary gas-phase activity, combined with a complete suppression of the self-sustained burning for the PA6/DTE-DOPO formulation.