Thermodynamics Isotope Effects of LaNi4.25Al0.75 Absorbing Protium,Deuterium and Tritium
The P-C-T curves of LaNi4.25Al0.75 alloy absorbing protium, deuterium and tritium were investigated at constant temperature and volume in our metal hydride research system. According to the Van’t Hoff Equation, the thermodynamics parameters of the hydride phase were determined. Enthalpy change and e...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | zho |
| Published: |
Editorial Board of Journal of Isotopes
2016-10-01
|
| Series: | Journal of Isotopes |
| Online Access: | http://www.tws.org.cn/CN/10.7538/tws.2016.29.02.0089 |
| Summary: | The P-C-T curves of LaNi4.25Al0.75 alloy absorbing protium, deuterium and tritium were investigated at constant temperature and volume in our metal hydride research system. According to the Van’t Hoff Equation, the thermodynamics parameters of the hydride phase were determined. Enthalpy change and entropy change for protium, deuterium and tritium were -44.5, -45.0, -47.1 kJ/mol and -118.0, -121.8, -127.5 J•mol-1•K-1. The experiments indicated that the isotope effect did not obviously at low temperature, however, as the temperature increasing to 100 ℃, there were obvious thermodynamics isotope effect with hydrogen absorption by LaNi4.25Al0.75 alloy. The order of equilibrium pressure absorbing gases was T2>D2>H2. However, the enthalpy and entropy appeared to be in verse order, T2>D2>H2. The results showed that hydrogen isotope effect with LaNiAl alloys were depended on temperature.
|
|---|---|
| ISSN: | 1000-7512 1000-7512 |