| Summary: | This investigation includes the use of 15% of glass wastes as a partial substitution to cement in combination with plastic wastes as volumetric replacement to natural coarse aggregate to produce sustainable concrete. Different volumetric replacements of plastic waste to natural coarse aggregate (25%, 50%, 75%, and 100%) were used in concrete containing 15% glass powder as a replacement by weight of cement. Generally, the results show that the inclusion of 15% glass powder improves the compressive strength, splitting tensile strength and flexural strength by about 13.3%, 36.3%, and 34.7%respectively at 60 day age in comparison with reference concrete without wastes, also the results show a decrease in water absorption and an increase in dry density. The inclusion of plastic waste aggregate in the presence of 15% glass powder leads to a decrease in the compressive strength, flexural strength, splitting tensile strength, dry density, ultrasonic pulse velocity, and thermal conductivity. The percentage reductions are 59.8%, 46.3%, 43.6%, 20.5%, 28.6%, and 54.4% respectively for concrete specimens that including 100% plastic waste coarse aggregate in comparison with concrete specimens without plastic waste aggregate.
|
|---|