| Summary: | Directionally solidified porous copper is considered as a potential candidate in the field of
microchannel heat sinks. By the Bridgman-type directional solidification method, a porous copper ingot was
fabricated. Evolution of the porosity, pore number density, average pore diameter and average interpore
spacing at different ingot heights was investigated. The results show that with the increase of ingot height,
the porosity firstly increases and then basically remains unchanged from the ignot height of 65 mm; the pore
number density rapidly decreases at first, and the decreasing speed becomes slower when the ignot height
higher than 85 mm; the average pore diameter increases and then remains unchanged from the ingot height
of 85 mm; the average interpore spacing increases, and the increasing speed of average interpore spacing
becomes slower with the increase of height to higher than 85 mm. In order to study the evolution of diameter
and spatial distribution of pores, the distribution ranges of pore diameter, nearest-neighbor distance and radial
cumulative pore number were analyzed. As the ingot height increases, the distribution ranges of pore diameter
and nearest-neighbor distance firstly increase and then tend to be stable. There are no pore clusters and for
long distance, the spatial distribution of pores is uniform at different ingot heights. Pore structure and 3D pore
morphology of porous copper were observed with the help of light illumination and X-ray tomography. Pore
nucleation, pore interruption, pore coalescence, diameter change of pores and lateral displacement of pores
were found to exist in the pore structure.
|
|---|