Effect of Ferocene Concentration on the Percent Conversion and Molecular Weight of Poly(Methyl Methacrylate) Homopolymers
This research is addressing the effect of different ferrocene concentration (0.00, 2.15x10-3, 4.30x10-3, 8.60x10-3, and 12.9x10-3) on the bulk free radical polymerization of methyl methacrylate monomer in benzene using benzoyl peroxide as initiator. The polymerization was conducted at 60º C under fr...
| Main Author: | |
|---|---|
| Format: | Article |
| Language: | Arabic |
| Published: |
College of Science for Women, University of Baghdad
2017-06-01
|
| Series: | Baghdad Science Journal |
| Subjects: | |
| Online Access: | http://bsj.uobaghdad.edu.iq/index.php/BSJ/article/view/2366 |
| Summary: | This research is addressing the effect of different ferrocene concentration (0.00, 2.15x10-3, 4.30x10-3, 8.60x10-3, and 12.9x10-3) on the bulk free radical polymerization of methyl methacrylate monomer in benzene using benzoyl peroxide as initiator. The polymerization was conducted at 60º C under free oxygen atmosphere. The resulting polymers were characterized by FTIR.
The results were compared with the presence and absence of ferrocene at 10% conversion. The %conversion was 3.04% with no ferrocene present in the polymerization medium and its increase to 9.06 with a first lowest ferrocene concentration added, i.e. 2.15 x10-3mol/l. This was positively reflected on the poly(methyl methacrylate) molecular weight measured by viscosity technique, especially in the presence of ferrocene.
|
|---|---|