| Summary: | In this contribution, we explored the copolymerization of propylene with higher α-olefins, including 1-octene (C8) 1-dodecene (C12), 1-hexadecene (C16) and 1-eicosene (C20), by using a dimethyl pyridylamidohafnium catalyst. A series of copolymers with varied comonomer incorporation, high molecular weight and narrow molecular weight distribution were obtained at mild conditions. The effects of the insertion of the comonomers on the microstructure, thermal and final mechanical properties were systemically studied by <sup>13</sup>C NMR, wide-angle X-ray scattering, DSC and tensile test. Excellent mechanical performances were achieved by tuning the incorporation and chain length of the higher α-olefins. When the comonomer content reached above 12 mol.%, polypropylene-based elastomers were obtained with high ductility. A combination of excellent elastic recovery and flexibility was achieved for the P/C16 copolymers with about 20 mol.% monomer incorporation. The monomer incorporation and side chain length played a crucial role in determining the mechanical property of the outstanding polypropylene-based elastomers.
|
|---|