Sample preparation and varistor physical properties measurement of ZnO+0.01Sb2O3

Sample preparation and varistor physical properties measurement of ZnO+0.01Sb2O3

The disc-shape ZnO+0.01Sb2O3 samples were prepared by standard ceramic techniques. The sample indicates white colour and was characterized by XRD. The prepared sample is varistor which shows breakdown field strength of 87.18 V/mm and non-linearity exponent (α) of 38.179. It is worth noting that the...

Full description

Bibliographic Details
Main Authors: Juggaroen, N, Casol, W., Panmatarith, T.
Format: Article
Language:English
Published: Prince of Songkla University 2003-01-01
Series:Songklanakarin Journal of Science and Technology (SJST)
Subjects:
varistor
ZnO+0.01Sb2O3
Online Access:http://www.sjst.psu.ac.th/journal/25_1_pdf/13thong_varis.pdf
id doaj-66bd9f3bb3db48678888d585010feba0
record_format Article
spelling doaj-66bd9f3bb3db48678888d585010feba02020-11-25T00:13:27ZengPrince of Songkla UniversitySongklanakarin Journal of Science and Technology (SJST)0125-33952003-01-01251133140Sample preparation and varistor physical properties measurement of ZnO+0.01Sb2O3Juggaroen, NCasol, W.Panmatarith, T.The disc-shape ZnO+0.01Sb2O3 samples were prepared by standard ceramic techniques. The sample indicates white colour and was characterized by XRD. The prepared sample is varistor which shows breakdown field strength of 87.18 V/mm and non-linearity exponent (α) of 38.179. It is worth noting that the high electric field strength of 5128.2 V/mm causes sample resistance changing. Sample resistance before and after poling were 189.13 kΩ and 6.516 kΩ, respectively.http://www.sjst.psu.ac.th/journal/25_1_pdf/13thong_varis.pdfvaristorZnO+0.01Sb2O3
collection DOAJ
language English
format Article
sources DOAJ
author Juggaroen, N
Casol, W.
Panmatarith, T.
spellingShingle Juggaroen, N
Casol, W.
Panmatarith, T.
Sample preparation and varistor physical properties measurement of ZnO+0.01Sb2O3
Songklanakarin Journal of Science and Technology (SJST)
varistor
ZnO+0.01Sb2O3
author_facet Juggaroen, N
Casol, W.
Panmatarith, T.
author_sort Juggaroen, N
title Sample preparation and varistor physical properties measurement of ZnO+0.01Sb2O3
title_short Sample preparation and varistor physical properties measurement of ZnO+0.01Sb2O3
title_full Sample preparation and varistor physical properties measurement of ZnO+0.01Sb2O3
title_fullStr Sample preparation and varistor physical properties measurement of ZnO+0.01Sb2O3
title_full_unstemmed Sample preparation and varistor physical properties measurement of ZnO+0.01Sb2O3
title_sort sample preparation and varistor physical properties measurement of zno+0.01sb2o3
publisher Prince of Songkla University
series Songklanakarin Journal of Science and Technology (SJST)
issn 0125-3395
publishDate 2003-01-01
description The disc-shape ZnO+0.01Sb2O3 samples were prepared by standard ceramic techniques. The sample indicates white colour and was characterized by XRD. The prepared sample is varistor which shows breakdown field strength of 87.18 V/mm and non-linearity exponent (α) of 38.179. It is worth noting that the high electric field strength of 5128.2 V/mm causes sample resistance changing. Sample resistance before and after poling were 189.13 kΩ and 6.516 kΩ, respectively.
topic varistor
ZnO+0.01Sb2O3
url http://www.sjst.psu.ac.th/journal/25_1_pdf/13thong_varis.pdf
work_keys_str_mv AT juggaroenn samplepreparationandvaristorphysicalpropertiesmeasurementofzno001sb2o3
AT casolw samplepreparationandvaristorphysicalpropertiesmeasurementofzno001sb2o3
AT panmataritht samplepreparationandvaristorphysicalpropertiesmeasurementofzno001sb2o3
_version_ 1725394132971552768

Similar Items