Hydrothermal Synthesis of SBA-15 Using Sodium Silicate Derived from Coal Gangue
Well-ordered SBA-15 was prepared with a hydrothermal route by sodium silicate derived from coal gangue. The as-prepared sample was analyzed by SAXRD, BET, TEM, and SEM, respectively. The results indicate that at a low hydrothermal temperature of 100∘C the well-ordered mesoporous SBA-15 could be synt...
| Main Authors: | , , , , |
|---|---|
| Format: | Article |
| Language: | English |
| Published: |
Hindawi Limited
2013-01-01
|
| Series: | Journal of Nanomaterials |
| Online Access: | http://dx.doi.org/10.1155/2013/352157 |
| Summary: | Well-ordered SBA-15 was prepared with a hydrothermal route by sodium silicate derived from coal gangue. The as-prepared sample was analyzed by SAXRD, BET, TEM, and SEM, respectively. The results indicate that at a low hydrothermal temperature of 100∘C the well-ordered mesoporous SBA-15 could be synthesized. The surface area, pore volume, and pore size of the sample are 552 m2/g, 0.54 cm3/g, and 7.0 nm, respectively. It is suggested that coal gangue could be used in obtaining an Si source to prepare mesoporous materials, such as SBA-15. |
|---|---|
| ISSN: | 1687-4110 1687-4129 |