| Summary: | This study has focused on the development of porous materials from representative Tunisian clay. The first step was the characterization of the clay through powder X-ray diffraction (XRD), thermal analysis and evaluation of its plasticity. With this data, an extrusion paste was prepared, mixing the clay with 26% water. This paste was extruded in the form of a tube and after a study of its thermal behavior; it was sintered at 850 °C for 2 h. The behavior of the prepared membranes was evaluated by measuring their porosity, permeability and mechanical strength mainly. The membranes thus obtained showed an acceptable porosity of about 36%, with a pore diameter of about 30 nm and mechanical strength of 12 MPa. Resumen: Este estudio se ha centrado en el desarrollo de materiales porosos a partir de arcillas representativas de Túnez. El primer paso consistió en la caracterización de la arcilla mediante difracción de rayos X (DRX), el análisis térmico y la evaluación de su plasticidad. Con estos datos, se preparó una pasta de extrusión, mezclando la arcilla con 26% de agua. Esta pasta se extruyó en forma de tubo y, tras un estudio de su comportamiento térmico, se consolidó a 850° C durante 2 hrs. El comportamiento de las membranas preparadas se evaluó midiendo su porosidad, permeabilidad y resistencia mecánica fundamentalmente. Las membranas obtenidas mediante este procedimiento mostraron una porosidad aceptable, de aproximadamente el 36%, con un diámetro de poro de aproximadamente 30 nm y una resistencia mecánica de 12 MPa. Keywords: Clay, Membranes, Mechanical properties, Porosity, Palabras clave: Arcilla, Membranas, Propiedades mecánicas, Porosidad
|
|---|