DEGRADASI ZAT WARNA NAPHTOL BLUE BLACK SECARA SONOLISIS DAN FOTOLISIS DENGAN PENAMBAHAN TIO2-ANATASE

• Main Authors: Safni -, Maizatisna -, Zulfarman -, T. Sakai
• Format: Article
• Language: Indonesian
• Published: Department of Chemistry, Faculty of Mathematics and Natural Sciences, Universitas Andalas 2015-02-01
• Series: Jurnal Riset Kimia
• Online Access: http://jrk.fmipa.unand.ac.id/index.php/jrk/article/view/66

ABSTRACT Degradation of naphtol blue black dye had been done by sonolysis and photolysis with adding anatase-TiO2. Sonolysis method were performed using an ultrasound with frequency 45 kHz, and photolysis using an irradiation of UV light l= 359 nm.  The optimum condition for degradation of 6 mg/L naphtol blue black by sonolysis with addition of 0.1000 g anatase-TiO2 were found at pH = 3.0 and temperature 30 ± 1°C.  Percentage of degradation at pH and temperature optimum was 65.20% within 120 minutes treatment.  Degradation of 6 mg/L naphtol blue black by photolysis with addition of 0.1000 g anatase-TiO2 was optimum at pH=3.0 and percentage of degradation was 68.72% within 120 minutes irradiation without stirring. The combine of sonolysis and photolysis method simultaneously for degradation of naphtol blue black dye by adding anatase-TiO2, achieved 92.51% degradation after 60 minutes treatment.   Keywords : sonolysis, photolysis, naphtol blue black